Our company is a leading stockiest and supplier of an entire rage of following products-
1. EN47 / 50CRV4 GRADE SHEET, PLATES, COILS
2. C-55 / EN9 / C62 GRADES SHEETS, PLATES, COILS
3. EN42J / C80/ C75 GRADE SHEET, PLATES, COILS
4. EN8/C-45 / C40 GRADES SHEET, PLATES, COILS
5. EN-19/40CRMO4 GRADES SHEET, PLATES, COILS
6. HARDENED TEMPERED SPRING STEEL STRIPS IN EN-9/C-55, EN-42J/C-80, EN-47/50CRV4, C-62, COIL AND SHEETS
Advantages of working with us:
We can help you source the material from the best companies and different makes.
We also guarantee quality assurance by providing the Test Certificate of the said products.
We are offering different variants at a very competitive and an affordable price.
Please feel free to contact our enthusiastic team to provide you with any additional information that you may require.
Looking forward for a long-term business relationship with you.
Mr Shahbaz Ahmed {Proprietor}
Mob – 7498271968/ 9082112378
Email – bombaysalescorp1@gmail.com
Web – www.bombaysalescorp.com , www.bombaysales.co.in, www.bombaysalescorp.in , www.carbonsteelplate.co.in
Reg Add– Shop No A5, Bharat Lokhand Bazar 1st Lane Ms Ali Road Near Two Tank Opp Kumbharwada Grant Road East Mumbai - 400008
Product Details:
Minimum Order Quantity | 500 Kg |
Material Grade | High Manganese Steel Plate |
Type | PLATE |
Brand | INDIAN |
Size | 1250MMX2500MM/5000MM |
Material | High Manganese Steel Plate |
Usage/Application | Shot Blast Equipment Liners - Abrasive,Non-Magnetic Applications - RR Bolster Plates |
Shape | PLATE |
Surface Finishing | BRIGHT |
Standard | INDIAN |
Country of Origin | Made in India |
WARRIORS ACRONI, X12, 11- 14 % MANGANESE PLATE WARRIORS ACRONI, X12, 11- 14 % Manganese is a true Hadfield Austenitic Manganese steel for resistance to severe impact and abrasive wear. It is work hardening steel.
WORK HARDENING refers to the fact that the steel becomes harder and harder the more it is impacted or compressed.
The “Hadfield” grade has an original hardness of approximately 220 Brinell. With continued impact and /or compression it will surface harden to over 550 Brinell. It should be noted that only the outer skin surface hardens. The under layer remains highly ductile and tough. As the surface wears, it continually renews itself becoming harder and harder.
Manganese steel is austenitic steel which means it is non-magnetic. This property makes it useful in many applications such as bottom plates for lifting magnets – separator drum shells for magnetic materials – wear shoes on electric brakes etc
CHEMCIAL COMPOSITION
Typical Mechanical Properties
Hardness (As Delivered) | 250 BHN |
Tensile Strength | 1, 32,000 PSI Min |
Yield Strength | 90,000 PSI Min |
After work Hardening | 550 BHN |
Note: Actual field results may vary depending upon the application and overall conditions of use.
ADVANTAGES
• Resistance to high abrasion and severe impact
• Capacity of cold work hardening hardness to 550 BHN
• To increase hardness from 200BHN (in as delivered plate) up to an in-service hardness of at least 600BHN.
• Have non-magnetic properties.
• Provide Maximum Wear Life.
• Exceptionally high toughness & ductility.
• Easy gas cutting & good weld ability
APPLICATION
MANGANESE ADVANTAGES
WORK HARDENING refers to the fact that the steel becomes harder and harder the more it is impacted or compressed.
The “Hadfield” grade has an original hardness of approximately 220 BRINELL. With continued impact and /or compression it will surface harden to over 550 BRINELL.
It should be noted that only the outer skin surface hardens. The under layer remains highly ductile and tough. As the surface wears, it continually renews itself becoming harder and harder.
Manganese steel is austenitic steel which means it is non-magnetic. This property makes it useful in many applications such as bottom plates for lifting magnets – separator drum shells for magnetic materials – wear shoes on electric brakes etc.
FORM OF SUPPLY
THICKNESS RANGE: 5 MM up to 100 MM range as per following divisions and thickness tolerance.
WIDTH RANGE:1000 MM up to 2000 MMhowever we can slit as per customers requirement.
EDGE CONDITION:Mill Edge, Sheared Edge
SHEET FORM:Material can be supplied in sheet form as well
We Accept Orders For Other Specific Thickness. However The Order Quantity And Lead Time For Supply Is To Be Confirmed By Us.
Additional Information:
Product Details:
Minimum Order Quantity | 500 Kg |
Material Grade | HIGH MANGANESE PLATE |
Type | SHEET |
Size | 1250MMX5000MM |
Material | 14% Manganese Plate |
Brand | IMPORTED |
Standard | IMPORTED |
Packaging Type | STANDARD |
Shape | SHEET / PLATE |
Color | BLACK |
Thickness | 4MM TO 20MM |
Usage/Application | crushers, hammers or pulverizes, cutting edges of large excavators, liners of shotblasting units, co |
Finishing | BLACK |
Hardness | ANNEALED |
I Deal In | New Only |
Finish | BLACK |
Length | 5000MM |
Width | 1250MM |
Country of Origin | Made in India |
This high manganese grade is an excellent work hardening, abrasion resistant steel. This steel is a non magnetic austenitic type, supplied in full plates or as profiled pieces by plasma cutting. Suitable for wear applications where high impact/gouging abrasion leads to a work hardening effect.
High manganese steel plate becomes increasingly hard when the surfaces of components are subject to repeated impact or abrasion. Its toughness, derived from high tensile strength and ductility, enables shock leads to be absorbed safely. Lack of lubrication or the intrusion of grit or sand particles does not seriously impair the wearing surfaces of components in contact. These characteristics combine to make high manganese steel plate ideal steel for use as wearing plates in those situations where abrasion, impact, or lubrication difficulties are encountered. The steel has the unique property in service of rapidly developing a work hardened surface while retaining its tough interior.
Wear Resistance of Manganese Plate
Severe wear on the surface has a work-hardening affect on the austenitic structure of this steel. This leads to an increase from the initially low hardness (about 200 BHN) to a service hardness of at least 500 BHN. This work-hardening maintains itself through in-service life. The underlay’s not work-hardened maintain a very high resistance to shock.
Properties
Brinell Hardness 200(approx.)
Tensile Strength 880 N/mm²
Yield Strength 320 N/mm
Elongation 40%
Typical Uses
The rapidity with which Manganese Plate hardens make this steel grade suitable for applications where the components must resist wear under conditions of sliding contact, often coupled with heavy pressure and repeated impact. Typical applications are wearing plates, stone or iron chutes, industrial trackwork, anti drill plates such as security doors, shot blasting equipment and tumbling machines.
Manganese Plate is the ideal solution for cases where severe wear is combined with shocks or high pressure capable of work-hardened its austenitic structure. Used in jaws of crushers, hammers or pulverizes, cutting edges of large excavators, liners of shotblasting units, cores and wall of parpen moulds, and screens.